J. D. Watson, S. Mondal, G. Gardner, G. A. Csáthy, M. J. Manfra
We report on the growth and electrical characterization of a series of two-dimensional hole systems (2DHSs) used to study the density dependence of low temperature mobility in 20 nm GaAs/AlGaAs quantum wells. The hole density was controlled by changing the Al mole fraction and the setback of the delta-doping layer. We varied the density over a range from 1.8 $\times$ 10$^{10}$ cm$^{-2}$ to 1.9 $\times$ 10$^{11}$ cm$^{-2}$ finding a nonmonotonic dependence of mobility on density at T = 0.3 K. Surprisingly, a peak mobility of 2.3 $\times$ 10$^6$ cm$^2$/Vs was measured at a density of 6.5 $\times$ 10$^{10}$ cm$^{-2}$ with further increase in density resulting in reduced mobility. We discuss possible mechanisms leading to the observed non-monotonic density dependence of the mobility. Relying solely on interface roughness scattering to explain the observed drop in mobility at high density requires roughness parameters which are not consistent with measurements of similar electron structures. This leaves open the possibility of contributions from other scattering mechanisms at high density.
View original:
http://arxiv.org/abs/1203.4312
No comments:
Post a Comment